Ceramvar alliage Vacon20
PricisionAlloy4J33/4J34(YB/T5234-1993)
* Ceramvaralloy, ASTMF1466, (Fe-Ni27-Co25), Chinese4J33/4J34
MainApplication:Matchwiththeelectricityvacuumindustrywiththeceramicstosealmeets.
Renvoi :
Grade |
Russie |
ÉTATS-UNIS D’AMÉRIQUE. |
Japon |
Allemagne |
4J33 |
33Hk(Ni33Co17) |
- |
KV-4(Ni33Co17) |
- |
4J34 |
31HK(Ni31Co20)24HK(Ni25Co18) |
Ceramvar(Ni27Co25) |
- |
Vacon20(Ni28Co20) |
Gradeandamp ; ChemicalComposition(SeeTable1)
Table1Gradeandamp ; ChemicalComposition
Grade |
ChemicalComposition(%) |
|||||||
C |
P |
S |
Mn |
Si |
Ni |
Co |
Fe |
|
≤ | ||||||||
4J33 |
0.05 |
0.020 |
0.020 |
0.50 |
0.30 |
32.1~33.6 |
14.0~15.2 |
Balance |
4J34 |
0.05 |
0.020 |
0.020 |
0.50 |
0.30 |
28.5~29.5 |
19.5~20.5 |
Balance |
Notes :
Underconditionthattheaveragecoefficientofthelinearexpansionmeetstherequirementso
norme, thecontentofnickelandcobaltareallowedtodeviatefromthestatedrange.
2.TheshapeanddimensionsofthealloysareincompliancewithGB/T14985.
MechanicalProperties(SeeTable2—Table4)
Table2TensileStrength(forwires)
Symbole |
État |
TensileStrength |
R |
Recuit |
andlt ; 585 |
1 |
Pour |
andgt ; 860 |
Table3TensileStrength(forStrips)
Symbole |
État |
TensileStrength/MPa |
R |
Recuit |
andlt ; 570 |
l |
Pour |
andgt ; 700 |
Table4HardnessofDeepStampingStrips
État |
Épaisseur |
HardnessHV |
Emboutissage profond |
andgt ; 2,5 |
≤170 |
≤2.5 |
≤165 |
PhysicalProperty (SeeTable5andamp ; Tableau6)
Table5LinearExpansionCofficient
Grade |
Heattreatmentofthesamples |
MeanCoefficientofLinearExpansionã/(10-6/K) |
|||
20 ~ 300° C |
20 ~ 400° C |
20 ~ 500° C |
20 ~ 600° C |
||
4J33 |
Heatto900±20 ° Cintheprotectiveatmosphereorinvacuumcondition, holdfor1hour, cooledto200 ° Cataratelessthan5 ° C/h, andtakeoutfromthefurnace. |
6.0~6.8 |
6.6~7.4 |
||
4J34 |
6.3~7.1 |
7.8~8.5 |
Table6TypicalCoefficientofLinearExpansion
Grade |
MeanCoefficientofLinearExpansionatDifferentTemperatureã/(10-6/K) |
||||
20 ~ 200° C |
20,300 ° C |
20 ~ 400° C |
20 ~ 500° C |
20 ~ 600° C |
|
4J33 |
7.1 |
6.5 |
6.3 |
7.1 |
8.5 |
4J34 |
7.5 |
6.9 |
6.6 |
6.9 |
8.3 |
Remarque : Thevaluesinthetablesareforreferenceonly.
Spécification : feuille / plaque, Bar/tige/câble/bobine, capillaire/tuyau
SizeRange :
1.Sheet---Thickness0.1 mm ~ 3.5 mm, largeur : ≤300mm, brightannealed lumineux, Condition : coldrolled,
2.plate---Thickness3.5 mm ~ 40,0 mm, largeur : ≤300mm, Condition : coldrolled, laminées à chaud, recuit
3.RoundWire---Dia0.1 mm ~ Dia5.0 mm, Condition : étirées, vif, brightannealed
4.FlatWire---Dia0.5 mm ~ Dia5.0 mm, longueur : ≤1000mm, Condition : plats, brightannealed
5.bar---Dia5.0 mm ~ Dia8.0 mm, longueur : ≤2000mm, brightannealed lumineux, Condition : tréfilé,
---Dia8.0 mm ~ Dia32.0 mm, longueur : ≤3000mm, Condition : laminées à chaud, lumineux, brightannealed
---Dia32.0 mm ~ Dia180.0 mm, longueur : ≤1300mm, Condition : hotforging, Pelé, tourné, hottreated
6.capillary---OD8.0 mm ~ 1,0 mm, ID0.1 mm ~ 8,0 mm, longueur : ≤2500mm, brightannealed lumineux, Condition : tréfilé,
7.pipe---OD120mm ~ 8,0 mm, ID8.0 mm ~ 129 mm, longueur : ≤4000mm, brightannealed lumineux, Condition : tréfilé,